Iron
Fe
Bal.
Nickel
Ni
10.0~14.0%
Chromium
Cr
16.0~18.0%
Molybdenum
Mo
2.0~3.0%
Manganese
Mn
≤2.0%
Silicon
Si
≤1.0%
Carbon
C
≤0.3%
Phosphorus
P
≤0.045%
Sulphur
S
≤0.03%
AISI 316L is a derivative of 18-8 type austenitic stainless steel, with 2 to 3% of Mo added. The Mo content of 316L makes this steel with excellent resistance to pitting corrosion and can be safely used in environments containing Cl- and other halogen ions. Based on its excellent corrosion resistance, it has a wide range of applications in the chemical industry.
AISI 316L Physical performance
Yield Strength |
Tensile strength |
Elongation |
Brinell hardness |
Rate of reduction in area |
Density |
Specific heat capacity |
Mpa,≥ |
Mpa,≥ |
%,≥ |
HB |
ψ (%) |
g/cm3 |
20℃,KJ·kg-1K-1 |
175 |
480 |
40 |
≤187 |
≥50 |
7.98 |
0.502 |
Thermal conductivity(W·m-1·K-1) |
100℃ |
300℃ |
500℃ |
15.1 |
18.4 |
20.9 |